PL spectra of GQDs (a), PEI1800 GQDs (b), and PEI600 GQDs (c) at different excitation wavelengths. Inset: photograph of aqueous solution of these three GQDs under room light (left) and 365 nm UV irradiation lamp (right). UV-vis absorption spectra (d) of GQDs, PEI1800 GQDs, and PEI600 GQDs dispersed in water. (© ACS)
Graphene quantum dots (GQDs) show great potential in the fields of photoelectronics, photovoltaics, biosensing, and bioimaging owing to their unique photoluminescence (PL) properties, including excellent biocompatibility, low toxicity, and high stability against photobleaching and photoblinking.
However, further development of GQDs is limited by their synthetic methodology and unclear PL mechanism. Therefore, it is urgent to find efficient and universal methods for the synthesis of GQDs with high stability, controllable surface properties, and tunable PL emission wavelength.In new work reported in ACS Applied Materials & Interfaces (“Red, Yellow, and Blue Luminescence by Graphene Quantum Dots: Syntheses, Mechanism, and Cellular Imaging”), researchers in China have synthesized PL-tunable GQDs with blue, yellow, and red emission colors by coating with polyethyleneimine (PEI) of different molecular weights.
PL spectra of GQDs (a), PEI1800 GQDs (b), and PEI600 GQDs (c) at different excitation wavelengths. Inset: photograph of aqueous solution of these three GQDs under room light (left) and 365 nm UV irradiation lamp (right). UV-vis absorption spectra (d) of GQDs, PEI1800 GQDs, and PEI600 GQDs dispersed in water. (© ACS) (click on image to enlarge)
Read More About a Company Commercializing Graphene Quantum Dots
Dotz Nano Ltd. is the world’s premier manufacturer of Graphene Quantum Dots (GQDs), commercializing an innovative technology that produces GQDs out of Coal and Carbon sources. Dotz Nano can supply high quality GQDs for use in a variety of applications that include:
- Medical imaging
- Displays/Consumer Electronics
- Optical brighteners
- Energy Storage
- Solar Cell
- Data Storage
With its modern labs and manufacturing facility, Dotz Nano is capturing the market utilizing GQDs as an alternative material in hundreds of applications.
(continued from above)
The team employed TEM, AFM, XRD, FTIR, XPS, DLS, and zeta potential to characterize the structures of the as-prepared GQDs and they stufied the PL mechanism by theoretical calculations.The average sizes of uncoated yellow-emitting GQDs, blue-emitting PEI1800 GQDs, and red-emitting PEI600 GQDs were 2.37, 6.05, and 57.31 nm, respectively. The yellow-emitting and blue-emitting GQDs were monolayer structures, whereas the red-emitting GQDs were multilayer structures. The red-emitting GQDs possessed a big PEI cage with multiple GQDs inside, whereas the blue-emitting PEI-coated GQDs had a single GQD core.The scientists found that carboxyl groups were changed to amide groups on the surface of GQDs and that this amidation reaction was crucial for PL change. By analyzing the molecular orbital and charge density, it was found that amide bonds decreased the conjugation and increased the energy gap thus inducing the blue shift of the PL.For the red-emitting GQDs, the conjugation area was enlarged by the interaction of GQDs in the PEI cage; thus, the PL peak exhibited a red shift.Remarkably, as the team points out, all GQDs exhibited good stability at high ionic strength and resisted photobleaching. Cell viability after treatment with the as-prepared GQDs indicated that GQDs had quite low cytotoxicity.”The GQDs could be used for bioimaging and are expected to be widely applied in multicolor imaging and bioanalysis applications,” the authors cocnlude their report. “We hope that this work will inspire the design of even better GQDs with tunable PL properties.”
Primary Story Contributed by Micheal Berger Nanowerk